以下为美国杜邦LCP 6130塑胶材料物性表：
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 吸水率 | --- | --- | 0.002 | % | |
| CTI UL标准值 | --- | --- | 4 | --- | ||
| 物理性能 | 纤维含量 | --- | --- | 30 | % | |
| 比重 | --- | --- | 1.62 | --- | ||
| 机械性能 | 引张强度 | --- | --- | 150 | MPa | |
| 拉伸强度 | --- | --- | 2.7 | % | ||
| 弯曲强度 | --- | --- | 170 | MPa | ||
| 弯曲弹性率 | --- | --- | 12 | GPa | ||
| 冲击强度 | --- | --- | 120 | j/m | ||
| 洛氏硬度 | --- | --- | 108 | R | ||
| 电气性能 | 诱电率 | --- | --- | 3.9 | --- | |
| 绝缘破坏电压 | --- | --- | 26 | MV/m | ||
| 加工性能 | 成形收缩率 | 流动方向 | --- | --- | 0 | % |
| 垂直方向 | 0.5 | % | ||||
| 热 性 能 | 线膨胀系数 | --- | --- | 1.3(3.7) | 10-5k | |
| 热变形温度 | 0.46Mpa | --- | 277 | ºC | ||
| 热变形温度 | 1.82Mpa | --- | 265 | ºC | ||
| 燃烧性 | --- | --- | V-0（0.2) | --- | ||